Analisis Pengujian Bending Komposit Serat Sabut Kelapa (Cocos Nucifera) Dengan Matriks Polyester Sebagai Bahan Cover Intake Manifold
DOI:
https://doi.org/10.32486/jeecae.v9i1.725Keywords:
komposit, Serat Sabut Kelapa, Polyester, uji bending, cover intake manifold, plastikAbstract
Composites are formed from a combination of fiber and matrix. Fiber functions as a reinforcing material that makes up the composite. The matrix functions to bind the fibers. Composites are useful as alternative materials such as iron, steel, metal and ceramic because they have advantages including biodegradability and corrosion resistance, making composites a potential new material to be developed. This research focuses on analyzing coconut fiber composites with a polyester resin matrix with varying fiber volume fractions of 30%, 35% and 40% using the hand lay-up method to determine the mechanical properties through the ASTM D790 Bending test. The highest average bending strength value is 65.32 N/mm^2, namely at a coconut fiber volume fraction of 40%. The best results from benchmark bending testing in making Intake Manifold Cover products to minimize the use of plastic materials in vehicle components.
References
Arsyad, M., & Salam, A. 2017. Analisis Pengaruh Konsentrasi Larutan Alkali Terhadap Perubahan Diameter Serat Sabut Kelapa. Journal INTEK. 4:11–13
Bifel, R. D. N., Maliwemu, E. U. K., Adoe, D. G. H., Adisucipto, J., & Ntt, P.-K. 2015. Pengaruh Perlakuan Alkali Serat Sabut Kelapa terhadap Kekuatan Tarik Komposit Polyester. LONTAR Jurnal Teknik Mesin UNDANA 02(01): 61-68
Bondra, M., Setiawan, A. P., Nilasari, P. F., & Siwalankerto, J. 2018. Penelitian Serabut Kelapa Sebagai Material Lantai Ecofriendly dan Biodegradable. JURNAL INTRA. 6(2): 431-436
Fajri, R. I., Tarkono, & Sugiyanto. 2013. Studi Sifat Mekanik Komposit Serat Sansevieria Cylindrica dengan Variasi Fraksi Volume Bermatrik Polyester. Jurnal FEMA. 1(2): 85–93
Gundara, G., & Nur Rahman, M. B. 2019. Sifat Tarik, Bending dan Impak Komposit Serat Sabut Kelapa-Polyester dengan Variasi Fraksi Volume. JMPM (Jurnal Material dan Proses Manufaktur). 3(1): 10–19
Manurung, C., & Napitupulu, R. 2015. Pengaruh Jenis Sebaran Serat pada Komposit Serat Tebu dan Resin Poliester Terhadap Sifat Mekanis. Majalah Ilmiah Politeknik Mandiri Bina Prestasi. 4(1): 29–37
Maskun, M., Assidiq, H., Bachril, S. N., & Al Mukarramah, N. H. 2022. Tinjauan Normatif Penerapan Prinsip Tanggung Jawab Produsen dalam Pengaturan Tata Kelola Sampah Plastik di Indonesia. Bina Hukum Lingkungan, 6(2), 184–200.
Pratama, Y. Y., & Setyanto, R. H. 2014. Pengaruh Perlakuan Alkali, Fraksi Volume Serat, dan Panjang Serat Terhadap Kekuatan Tarik Komposit Serat Sabut Kelapa - Polyester. Jurnal Ilmiah Teknik Industri, 13(1): 8-15
Rahmawaty, S. A. 2021. Analisa Kekuatan Tarik dan Tekuk pada Komposit Fiberglas-Polyester Berpenguat Serat Gelas dengan Variasi Fraksi Volume Serat. JTM-ITI (Jurnal Teknik Mesin ITI). 5(3): 146–155
Rizaldi, F. A. 2023. Analisa Pengaruh Perendaman NaOH dan Fraksi Volume dengan Resin Polyester Terhadap Kekuatan Tarik dan Bending pada Komposit Serat Sabut Kelapa. JTM. 11(03): 27-34.
Sundari, E., Karmin, Fenoria Putri, & Budiman, A. 2023. Analisa Pengaruh Perlakuan Alkali Terhadap Sifat Mekanik Komposit Berpenguat Serat Buah Kelapa Sawit. MACHINERY JURNAL TEKNOLOGI TERAPAN. 4(2): 51-59
Zulkifli. 2018. Analisa Kekuatan Tarik dan Bentuk Patahan Komposit Serat Sabuk Kelapa Bermatriks Epoxy Terhadap Variasi Fraksi Volume Serat. 6.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2024 JEECAE (Journal of Electrical, Electronics, Control, and Automotive Engineering)
![Creative Commons License](http://i.creativecommons.org/l/by-sa/4.0/88x31.png)
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.